Chlorinated polyethylene CM352
CM352, Medium to low molecular weight, Mooney viscosity between 55 and 70, superior mechanical performances, applied in many fields and with good processibility.It is equivalent toTyrin CM0636 from Dow Chemical .
Tech Specs:
Items UNIT INDEX Test Method
Chlorine content % 35±1 ISO 7725
Heat of Fusion J/g ≤2.0 DSC
Volatile Matter component % ≤0.4 ISO 1269
Rate of filtration(40 mesh) % ≥98 --
Shore Hardness A ° ≤56 ISO 7619
Tensile strength Mpa ≥8.0 ISO 37
Elongation at break % ≥800 ISO 37
Mooney Viscosity ML(121°C 1＋4) -- 55-70 --
Whiteness E457 ° ≥80 --
Application: Low Viscosity grade, widely used for hose, wire / cable and molded products..Not only it can be used as halide rubber solely but also it can be mixed with CR, CSM, NBR, SBR and NR at any proportion.
Package : 25kg PP valve bag ; 25kg Woven bag with PE liner ; 500/550kg super sack The product can be stored under appropriate conditions for two years. But please keep products store in a dry ventilated environment (temperature should not exceed 30°C, in low humidity). Inappropriate storage environment may cause agglomeration.Especially at high temperatures & high humidity, it is recommended not to stack more than 30 days long, it may increase agglomeration phenomenon. Agglomeration does not affect the quality and performance , not a quality problem, but Agglomeration material is smashed before using . It is not dangerous cargo .You should handle the material according to the instruction described on MSDS.The MSDS is available from sales department once required.